Preparation, characterization and activation of Pd catalysts supported on CNx foam for the liquid phase decomposition of formic acid.

In this work, we have prepared a series of Pd catalysts on a CN x support for the liquid phase decomposition of formic acid. The structured CN x support was obtained through thermal pyrolysis of melamine foam and the pyrolysis conditions were optimized to achieve high surface area. The resulting support contains high amount of nitrogen with a contribution of pyridinic component. Several Pd catalysts were prepared and under optimized conditions, we were able to obtain small (2.7 ± 0.9) nm Pd particles by using the oxidized support in powdery form. The activity of the optimized catalyst was studied under different conditions in the fresh and the used form. The fresh catalyst did not show significant activity. However, we found that the catalyst activated after use. Activation was understood in terms of the variation of surface Pd oxidation states under the effect of formic acid/sodium formate solutions. We found that the best activity is achieved under an optimal proportion of Pd0/PdII surface states according to previous reports. Under the best conditions, the activity of the best catalyst (8.6Pd/CN 0.3) was as high as 9245 h−1, attributable to the small particle size, the Pd0/PdII ratio, the amount of pyridinic nitrogen, and the testing conditions, which included the preadsorption of sodium formate. [Display omitted] • We prepared CN x -supported Pd catalysts for the decomposition of formic acid. • The CN x support was obtained by thermal pyrolysis of melamine foam at 700 °C. • We obtained 2.7nm Pd particles on the oxidized CN 0.3 support under optimized conditions. • The optimized 8.6Pd/CN 0.3 catalyst was not very active but activated upon use. • Activation understood in terms of the variation of surface Pd0/PdII states after use. [ABSTRACT FROM AUTHOR]