Polymerization shrinkage, flexural and compression properties of low-shrinkage dental resin composites.

Park, JK ; Lee, GH ; et al.

In: Dental materials journal, Jg. 33 (2014), Heft 1, S. 104-10

academicJournal

This study evaluated the polymerization shrinkage, flexural and compressive properties of low-shrinkage resin composites. For the study, four methacrylate-based and one silorane-based resin composites were light cured using three different light-curing units (LCUs) and their polymerization shrinkage, flexural (strength (FS) and modulus (FM)) and compressive (strength (CS) and modulus (CM)) properties were evaluated. Data were statistically analyzed using ANOVA and a post-hoc Tukey test. The polymerization shrinkage ranged approximately 7.6-14.2 μm for 2-mm thick specimens depending on the resin product and LCU. Filtek LS showed the least shrinkage while the rest shrank approximately 13.2-14.2 μm. However, Filtek LS showed the greatest shrinkage difference for the used LCUs. FS and CS of the tested specimens ranged 96.2-152.1 MPa and 239.2-288.4 MPa, respectively, depending on the resin product and LCU. The highest and lowest FS and FM were recorded for the methacrylate-based resin composites. Among the specimens, Filtek LS showed the lowest CS and CM.

Titel:	Polymerization shrinkage, flexural and compression properties of low-shrinkage dental resin composites.
Autor/in / Beteiligte Person:	Park, JK ; Lee, GH ; Kim, JH ; Park, MG ; Ko, CC ; Kim, HI ; Kwon, YH
Zeitschrift:	Dental materials journal, Jg. 33 (2014), Heft 1, S. 104-10
Veröffentlichung:	Tokyo-to : Japanese Society for Dental Materials and Devices, [1982?-, 2014
Medientyp:	academicJournal
ISSN:	1881-1361 (electronic)
DOI:	10.4012/dmj.2013-126
Schlagwort:	Elastic Modulus Light-Curing of Dental Adhesives Materials Testing Polymerization Surface Properties Composite Resins chemistry
Sonstiges:	Nachgewiesen in: MEDLINE Sprachen: English Publication Type: Comparative Study; Journal Article Language: English [Dent Mater J] 2014; Vol. 33 (1), pp. 104-10. MeSH Terms: Composite Resins / *chemistry ; Elastic Modulus ; Light-Curing of Dental Adhesives ; Materials Testing ; Polymerization ; Surface Properties Substance Nomenclature: 0 (Aelite LS) ; 0 (Composite Resins) ; 0 (Estelite sigma) ; 0 (Filtek LS Low Shrink resin) ; 0 (Grandio) ; 0 (Venus flow composite resin) ; 0 (premise composite resin) Entry Date(s): Date Created: 20140205 Date Completed: 20151022 Latest Revision: 20190918 Update Code: 20240513

Klicken Sie ein Format an und speichern Sie dann die Daten oder geben Sie eine Empfänger-Adresse ein und lassen Sie sich per Email zusenden.

BibTeX Citavi, JabRef, u.a.
(Literaturverwaltung)

PDF kein Volltext!
(Merkzettel, Notizen)

RIS Endnote, Citavi u.a.
(Literaturverwaltung)

MODS
(XML zur Weiterverarbeitung)

oder

Wählen Sie das für Sie passende Zitationsformat und kopieren Sie es dann in die Zwischenablage, lassen es sich per Mail zusenden oder speichern es als PDF-Datei.

Gewünschter Zitations-Stil:

oder

Bitte prüfen Sie, ob die Zitation formal korrekt ist, bevor Sie sie in einer Arbeit verwenden. Benutzen Sie gegebenenfalls den "Exportieren"-Dialog, wenn Sie ein Literaturverwaltungsprogramm verwenden und die Zitat-Angaben selbst formatieren wollen.