Effect of Processing Conditions on Fracture Resistance and Cohesive Laws of Binderfree All-Cellulose Composites.
In: Applied Composite Materials, Jg. 21 (2014-12-01), Heft 6, S. 805-825
Online
academicJournal
Zugriff:
The fracture properties of all-cellulose composites without matrix were studied using Double Cantilever Beam (DCB) sandwich specimens loaded with pure monotonically increasing bending moments, which give stable crack growth. The experiments were conducted in an environmental scanning electron microscope to a) perform accurate measurements of both the fracture energy for crack initiation and the fracture resistance and b) observe the microscale failure mechanisms especially in the the wake of the crack tip. Since the mechanical behaviour of the all-cellulose composites was non-linear, a general method was first developed to obtain fracture resistance values from the DCB specimens taking into account the non-linear material response. The binderfree all-cellulose composites were prepared by a mechanical refinement process that allows the formation of intramolecular bonds between the cellulose molecules during the drying process. Defibrilation of the raw cellulose material is done in wet medium in a paper-like process. Panels with different refining time were tested and it was found than an increase in fibre fibrillation results in a lower fracture resistance. [ABSTRACT FROM AUTHOR]
Copyright of Applied Composite Materials is the property of Springer Nature and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)
Titel: |
Effect of Processing Conditions on Fracture Resistance and Cohesive Laws of Binderfree All-Cellulose Composites.
|
---|---|
Autor/in / Beteiligte Person: | Goutianos, S. ; Sørensen, B. F. ; Arévalo, R. ; Peijs, T. |
Link: | |
Zeitschrift: | Applied Composite Materials, Jg. 21 (2014-12-01), Heft 6, S. 805-825 |
Veröffentlichung: | 2014 |
Medientyp: | academicJournal |
ISSN: | 0929-189X (print) |
DOI: | 10.1007/s10443-013-9381-0 |
Sonstiges: |
|