Improvement on Conversion Efficiency of CIGS Thin Film Solar Cell Using Electrochemical Depleting.

In this work, electrochemical depleting, a reverse operation of electrochemical plating was adopted as an alternative of toxic KCN etching to conduct the surface modification process. The original CuInSe 2 absorber layers were fabricated following a traditional electrodeposition-annealing approach. After the CuInSe 2 and Cu(InGa)Se 2 films were annealed, the films were then put into a sulfuric acid solution and electrochemical etched to form a Cu-deficient absorber layer on top of the CuInSe 2 and Cu(InGa)Se 2 bulk. The thickness of the Cu-deficient absorber layer can be controlled by depleting time. The X-ray diffraction and Raman spectroscopy indicated the formation of the Cu-deficient CIGS phase on the absorber surface. The current-voltage curves of CuInSe 2 and Cu(InGa)Se 2 cells with a thick Cu-deficient absorber layer on the surface displayed a kink effect which was probably caused by the increase in series resistance and light absorption in the Cu-deficient absorber layer instead of junction region. The cells with a thin Cu-deficient absorber layer yielded higher efficiency of Cu(InGa)Se 2 cells. Through electrochemical depleting on the surface of absorbet layer of the Cu(InGa)Se 2 , the fill factor and the efficiency of the Cu(InGa)Se 2 solar cell is improved respectively from 58% to 65% and from 11.4% to 13.8%. [ABSTRACT FROM AUTHOR]

Copyright of Journal of The Electrochemical Society is the property of IOP Publishing and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)