Low-Temperature Magnetic Hysteresis in Nd(Pr)-Fe-B Nanostructured Alloys with Nd2Fe14B Type Main Phase Composition
In: Defect and Diffusion Forum, Jg. 386 (2018-09-01), S. 125-130
Online
unknown
Zugriff:
Magnetic hysteresis properties of nanostructured industrially manufactured Nd-Fe-B and Pr-Fe-B alloys on the base of a tetragonal Nd2Fe14B (2-14-1) hard magnetic phase (MQP-B, MQP-B+ and MQP-16-7 brands) have been investigated at 4.2 K in magnetic fields up to 58 T. The chemical composition of the alloys given in the certificates was defined more precisely. The grain sizes of the main 2-14-1 phase were determined. The average grain size is much smaller than a critical single domain diameter. Coercivity, remanence magnetization, saturation magnetization and maximal magnetic energy product were determined at 4.2 K and compared with those obtained at room temperature.
Titel: |
Low-Temperature Magnetic Hysteresis in Nd(Pr)-Fe-B Nanostructured Alloys with Nd2Fe14B Type Main Phase Composition
|
---|---|
Autor/in / Beteiligte Person: | Ivanov, L. A. ; Gorbunov, Denis ; Tereshina, I. S. ; Neznakhin, D.S. ; Politova, G. A. ; Volegov, A.S. ; Kudrevatykh, N. V. |
Link: | |
Zeitschrift: | Defect and Diffusion Forum, Jg. 386 (2018-09-01), S. 125-130 |
Veröffentlichung: | Trans Tech Publications, Ltd., 2018 |
Medientyp: | unknown |
ISSN: | 1662-9507 (print) |
DOI: | 10.4028/www.scientific.net/ddf.386.125 |
Schlagwort: |
|
Sonstiges: |
|