Alloy degradation in a co-firing biomass CFB vortex finder application at 880 °C

Lundberg, Mats ; Boström, Dan ; et al.

In: Corrosion Science, Jg. 150 (2019-04-01), S. 136-150

Online unknown

Zugriff:

Mechanisms of alloy degradation in a fireside N-S-O-C-H-Cl-Na-K atmosphere at 880 degrees C were elucidated using SEM-EDS, chemical equilibrium calculations, and XRD. Alloys 310S, 800H/HT, and 600 were studied after 0, 8000, and 16,000 h exposure in a boiler co-firing biomass waste. For 310S and 800H/HT it was shown that nitrogen formed internal Cr nitrides lowering the Cr activity and inhibiting internal alloy Cr permeation, and that NaCl and Na2SO4 reacted with Cr oxide to form chromate and to accelerate the S and the Cl pickup. Alloy 600 showed no nitride or major chromate formation. Bio4Energy

Titel:	Alloy degradation in a co-firing biomass CFB vortex finder application at 880 °C
Autor/in / Beteiligte Person:	Lundberg, Mats ; Boström, Dan ; Backman, Rainer ; Hagman, Henrik
Link:	View record in OpenAIRE (Volltext) E-Journal im Bestand der UB Hagen? https://doi.org/10.1016/j.corsci.2019.01.038
Zeitschrift:	Corrosion Science, Jg. 150 (2019-04-01), S. 136-150
Veröffentlichung:	Elsevier BV, 2019
Medientyp:	unknown
ISSN:	0010-938X (print)
DOI:	10.1016/j.corsci.2019.01.038
Schlagwort:	Materials science Sulfide 020209 energy General Chemical Engineering Alloy Biomass SO2 Vortex finder 02 engineering and technology engineering.material HCl Chloride Alloy 600 Energy engineering Corrosion Korrosionsteknik Atmosphere Cl 0202 electrical engineering, electronic engineering, information engineering Na General Materials Science Alloy 800H/HT Carbide CFB boiler Co-combustion Metallurgy Oxide Corrosion Engineering General Chemistry 021001 nanoscience & nanotechnology N-2 O-2 CO NH3 High-temperature corrosion Nitride engineering Alloy 310S Degradation (geology) CO2 Corrosion engineering Volatilization Chemical equilibrium 0210 nano-technology
Sonstiges:	Nachgewiesen in: OpenAIRE File Description: application/pdf Rights: OPEN

Klicken Sie ein Format an und speichern Sie dann die Daten oder geben Sie eine Empfänger-Adresse ein und lassen Sie sich per Email zusenden.

BibTeX Citavi, JabRef, u.a.
(Literaturverwaltung)

PDF kein Volltext!
(Merkzettel, Notizen)

RIS Endnote, Citavi u.a.
(Literaturverwaltung)

MODS
(XML zur Weiterverarbeitung)

oder

Wählen Sie das für Sie passende Zitationsformat und kopieren Sie es dann in die Zwischenablage, lassen es sich per Mail zusenden oder speichern es als PDF-Datei.

Gewünschter Zitations-Stil:

oder

Bitte prüfen Sie, ob die Zitation formal korrekt ist, bevor Sie sie in einer Arbeit verwenden. Benutzen Sie gegebenenfalls den "Exportieren"-Dialog, wenn Sie ein Literaturverwaltungsprogramm verwenden und die Zitat-Angaben selbst formatieren wollen.