Electrical properties of calcium doped BiFeO3 films on LaNiO3 coated Pt substrates
In: Processing and Application of Ceramics, Jg. 12 (2018), Heft 2, S. 153-163
academicJournal
Zugriff:
Pure and calcium-modified (CaxBi1-xFeO3, x = 0.0, 0.1, 0.2, 0.30) thin films were fabricated on Pt(111)/Ti/SiO2/Si substrates by the soft chemical method using LaNiO3 as the bottom electrode. Highly (200)-oriented BFO film was coherently grown on LNO at 500 °C. Ca-doped BiFeO3 films have a dense microstructure and rounded grains. The conventional problem of the leakage current for the highest doped film was reduced from 10-5 to 10-10 with remarkable improvement in the film/electrode interface, chemical homogeneity, crystallinity, and morphology of the BFO film. Enhanced ferroelectricity was observed at room temperature due to the bottom electrode. Fatigue-free films were grown on LaNiO3 bottom electrodes with no degradation after 1×1010 switching cycles at an applied voltage of 5 V with a frequency of 1 MHz. After several tests the capacitors retained 77% of its polarization upon a retention time of 104 s. Room temperature magnetic coercive field measurements indicate that the magnetic behaviour is influenced by the nature of the bottom electrode.
Titel: |
Electrical properties of calcium doped BiFeO3 films on LaNiO3 coated Pt substrates
|
---|---|
Autor/in / Beteiligte Person: | Lucas Fabricio Goncalves ; Leandro Silva Rosa Rocha ; Hangai, Bruno ; Pedro Paulo Silva Ortega ; Longo, Elson ; Simões, Alexandre Z. |
Link: | |
Zeitschrift: | Processing and Application of Ceramics, Jg. 12 (2018), Heft 2, S. 153-163 |
Veröffentlichung: | University of Novi Sad, 2018 |
Medientyp: | academicJournal |
ISSN: | 1820-6131 (print) ; 2406-1034 (print) |
DOI: | 10.2298/PAC1802153G |
Schlagwort: |
|
Sonstiges: |
|