A thermomechanical fatigue (TMF) cycle, intended to represent aeroengine blade working conditions, was selected for carrying out tests on uncoated and aluminide coated SRR99 samples until test piece failure. Optical images of the surface of test pieces were collected during testing to monitor surface crack initiation and accompanying transformations. Using these images, surface changes were quantified as a function of time. Post test each sample was taken through an incremental polishing procedure to allow damage in the tested material to be studied as a function of depth, using optical microscope-based quantitative metallography and scanning electron microscopy (SEM). The relationship between the observed surface changes and the damage built-up subsurface was examined. Differences in damage density on the surface and subsurface planes between coated and uncoated samples could accommodate the observed life reductions.

Titel:	Crack initiation in a coated and an uncoated nickel-base superalloy under TMF conditions
Autor/in / Beteiligte Person:	JOHNSON, P. K ; ARANA, M ; OSTOLAZA, K. M ; BRESSERS, J
Link:	View record from PASCAL Archive
Quelle:	Journal of engineering for gas turbines and power 120(4):792-795; Jg. 120 (1998) 4, S. 792-795
Veröffentlichung:	New York, NY: American Society of Mechanical Engineers, 1998
Medientyp:	Konferenz
Umfang:	print, 9 ref
ISSN:	0742-4795 (print)
Schlagwort:	Energy Énergie Mechanical engineering Génie mécanique Sciences exactes et technologie Exact sciences and technology Sciences appliquees Applied sciences Metaux. Metallurgie Metals. Metallurgy Propriétés mécaniques. Rhéologie. Mécanique de la rupture. Tribologie Mechanical properties and methods of testing. Rheology. Fracture mechanics. Tribology Rupture Fractures Genie mecanique. Construction mecanique Mechanical engineering. Machine design Moteurs et turbines Engines and turbines Moteurs à cycles continus: turbines à vapeur, à gaz, propulseurs à réaction Continuous cycle engines: steam and gas turbines, jet engines Alliage base nickel Nickel base alloys Aluminure Aluminides Aluminuro Amorçage fissure Crack initiation Iniciación grieta Risseinleitung Aube turbine Turbine blade Paleta turbina Turbinenschaufel Etude expérimentale Experimental study Estudio experimental Experimentelle Untersuchung Fatigue thermique Thermal fatigue Fatiga térmica Thermische Ermuedung Fatigue Fatiga Ermuedung Propriété thermomécanique Thermomechanical properties Propriedad termomecánica Revêtement céramique Ceramic coating Revestimiento cerámico Keramikbeschichten Revêtement diffusion Diffusion coatings Ruptura Bruch Superalliage Superalloy Superaléación Superlegierung Turboréacteur Turbojet Turboreactor
Sonstiges:	Nachgewiesen in: PASCAL Archive Sprachen: English Original Material: INIST-CNRS Document Type: Conference Paper File Description: text Language: English Author Affiliations: Joint Research Centre, European Commission, P.O. Box 2, 1755 ZG, Petten, Netherlands Rights: Copyright 1999 INIST-CNRS ; CC BY 4.0 ; Sauf mention contraire ci-dessus, le contenu de cette notice bibliographique peut être utilisé dans le cadre d’une licence CC BY 4.0 Inist-CNRS / Unless otherwise stated above, the content of this bibliographic record may be used under a CC BY 4.0 licence by Inist-CNRS / A menos que se haya señalado antes, el contenido de este registro bibliográfico puede ser utilizado al amparo de una licencia CC BY 4.0 Inist-CNRS Notes: Mechanical engineering. Mechanical construction. Handling ; Metals. Metallurgy

Klicken Sie ein Format an und speichern Sie dann die Daten oder geben Sie eine Empfänger-Adresse ein und lassen Sie sich per Email zusenden.

BibTeX Citavi, JabRef, u.a.
(Literaturverwaltung)

PDF kein Volltext!
(Merkzettel, Notizen)

RIS Endnote, Citavi u.a.
(Literaturverwaltung)

MODS
(XML zur Weiterverarbeitung)

oder

Wählen Sie das für Sie passende Zitationsformat und kopieren Sie es dann in die Zwischenablage, lassen es sich per Mail zusenden oder speichern es als PDF-Datei.

Gewünschter Zitations-Stil:

oder

Bitte prüfen Sie, ob die Zitation formal korrekt ist, bevor Sie sie in einer Arbeit verwenden. Benutzen Sie gegebenenfalls den "Exportieren"-Dialog, wenn Sie ein Literaturverwaltungsprogramm verwenden und die Zitat-Angaben selbst formatieren wollen.

Crack initiation in a coated and an uncoated nickel-base superalloy under TMF conditions