Importance de la cavitation lors de la fissuration en fatigue du caoutchouc naturel chargé / Cavitation influence on fatigue crack growth in filled natural rubber

LE CAM, Jean-Benoit ; PEROCHEAU, Franck ; et al.

In: Mécanique & industries, Jg. 7 (2006), Heft 2, S. 123-129

Online academicJournal - print, 14 ref

Zugriff:

Full Text Finder (Volltext)

Cavitation influence on fatigue crack growth in filled natural rubber. The aim of this present paper is the fractographic analysis of cracks in a carbon black filled natural rubber under fatigue loading conditions. In order to determine the crack growth mechanism, the microstructural state behind the crack tip should be analysed. Here, an experimental method that consists in cutting the crack tip during its observation with a scanning electron microscope is proposed. The crack tip opening is performed using two different energetic sources in order to break cross-links between the macromolecules. The first source is mechanical: the sample is stretched on a simple tensile apparatus. The second one is the electronic beam. Observation results indicate that cavitation is the fatigue damage which drives crack growth. The cavitation mechanism is initiated by the decohesion of the oxides and rubber matrix.

Titel:	Importance de la cavitation lors de la fissuration en fatigue du caoutchouc naturel chargé / Cavitation influence on fatigue crack growth in filled natural rubber
Autor/in / Beteiligte Person:	LE CAM, Jean-Benoit ; PEROCHEAU, Franck ; HUNEAU, Bertrand ; VERRON, Erwan ; GORNET, Laurent
Link:	Full Text Finder (Volltext) View record from PASCAL Archive
Zeitschrift:	Mécanique & industries, Jg. 7 (2006), Heft 2, S. 123-129
Veröffentlichung:	Paris: Elsevier, 2006
Medientyp:	academicJournal
Umfang:	print, 14 ref
ISSN:	1296-2139 (print)
Schlagwort:	Mechanical engineering Génie mécanique Mechanics acoustics Mécanique et acoustique Sciences exactes et technologie Exact sciences and technology Physique Physics Domaines classiques de la physique (y compris les applications) Fundamental areas of phenomenology (including applications) Mécanique des solides Solid mechanics Mécanique des structures et des milieux continus Structural and continuum mechanics Mécanique de la rupture (fissure, fatigue, endommagement...) Fracture mechanics (crack, fatigue, damage...) Sciences appliquees Applied sciences Industrie des polymeres, peintures, bois Polymer industry, paints, wood Technologie des polymères Technology of polymers Polymères industriels. Préparations Industrial polymers. Preparations Elastomères Elastomers Caoutchouc naturel Natural rubber Caucho natural Cavitation Cavitación Endommagement Damaging Deterioración Etude expérimentale Experimental study Estudio experimental Extrémité fissure Crack tip Extremidad fisura Fatigue Fatiga Fissure fatigue Fatigue crack Fisura fatiga Fractographie Fractography Fractografía Macromolécule Macromolecule Macromolécula Matériau composite Composite material Material compuesto Microfissure Microcrack Microfisura Microscopie électronique balayage Scanning electron microscopy Microscopía electrónica barrido Microstructure Microestructura Noir carbone Carbon black Carbón negro Propagation fissure Crack propagation Propagación fisura Rodage Breaking in Esmerilado Rupture fatigue Fatigue fracture Rotura fatiga Rubber igue / damage / crack growth / cavitation / fractography / micro-cut
Sonstiges:	Nachgewiesen in: PASCAL Archive Sprachen: French Original Material: INIST-CNRS Document Type: Article File Description: text Language: French Author Affiliations: Institut de Recherche en Génie Civil et Mécanique, École Centrale de Nantes, BP 92101, 44321 Nantes, France ; Allevard Rejna Autosuspensions, 201 rue Sin Le Noble, 59506 Douai, France Rights: Copyright 2006 INIST-CNRS ; CC BY 4.0 ; Sauf mention contraire ci-dessus, le contenu de cette notice bibliographique peut être utilisé dans le cadre d’une licence CC BY 4.0 Inist-CNRS / Unless otherwise stated above, the content of this bibliographic record may be used under a CC BY 4.0 licence by Inist-CNRS / A menos que se haya señalado antes, el contenido de este registro bibliográfico puede ser utilizado al amparo de una licencia CC BY 4.0 Inist-CNRS Notes: Physics: solid mechanics ; Polymer industry, paints, wood

Klicken Sie ein Format an und speichern Sie dann die Daten oder geben Sie eine Empfänger-Adresse ein und lassen Sie sich per Email zusenden.

BibTeX Citavi, JabRef, u.a.
(Literaturverwaltung)

PDF kein Volltext!
(Merkzettel, Notizen)

RIS Endnote, Citavi u.a.
(Literaturverwaltung)

MODS
(XML zur Weiterverarbeitung)

oder

Wählen Sie das für Sie passende Zitationsformat und kopieren Sie es dann in die Zwischenablage, lassen es sich per Mail zusenden oder speichern es als PDF-Datei.

Gewünschter Zitations-Stil:

oder

Bitte prüfen Sie, ob die Zitation formal korrekt ist, bevor Sie sie in einer Arbeit verwenden. Benutzen Sie gegebenenfalls den "Exportieren"-Dialog, wenn Sie ein Literaturverwaltungsprogramm verwenden und die Zitat-Angaben selbst formatieren wollen.