A parametric study on the design of stitched laminated DCB specimens

XIANNIAN, SUN ; WOOD, Michael D. K ; et al.

In: Thirteenth international conference on composite structures, Melbourne, 14-16 November 2005Composite structures 75(1-4):72-78; Jg. 75 (2006) 1-4, S. 72-78

Konferenz - print, 10 ref

Wie komme ich dran?

Through-the-thickness stitching has been shown to have the capacity of improving the poor interlaminar toughness of laminated composites for many years. Double cantilever beam (DCB) testing has been used to assess the enhanced delamination toughness of stitched laminates. To avoid the premature flexure failure of delaminated substrate beams, thick tabs are bonded to either side of the standard DCB specimens. Consequently, higher opening load can be applied to the stitched tabbed DCB (TDCB) specimens to propagate the delamination crack due to the enlarged bending stiffness and strength. This creates a significant bending of the loading pin, which needs to be accounted for in the numerical analysis. In this paper, a parametric analysis was conducted to investigate the effect of reinforcing tab thickness on the measured and predicted delamination toughness.

Titel:	A parametric study on the design of stitched laminated DCB specimens
Autor/in / Beteiligte Person:	XIANNIAN, SUN ; WOOD, Michael D. K ; LIYONG, TONG
Link:	E-Journal im Bestand der UB Hagen? View record from PASCAL Archive
Quelle:	Thirteenth international conference on composite structures, Melbourne, 14-16 November 2005Composite structures 75(1-4):72-78; Jg. 75 (2006) 1-4, S. 72-78
Veröffentlichung:	Oxford: Elsevier Science, 2006
Medientyp:	Konferenz
Umfang:	print, 10 ref
ISSN:	0263-8223 (print)
Schlagwort:	Mechanics acoustics Mécanique et acoustique Sciences exactes et technologie Exact sciences and technology Physique Physics Domaines classiques de la physique (y compris les applications) Fundamental areas of phenomenology (including applications) Mécanique des solides Solid mechanics Mécanique des structures et des milieux continus Structural and continuum mechanics Mécanique de la rupture (fissure, fatigue, endommagement...) Fracture mechanics (crack, fatigue, damage...) Sciences appliquees Applied sciences Industrie des polymeres, peintures, bois Polymer industry, paints, wood Technologie des polymères Technology of polymers Formes d'application et semiproduits Forms of application and semi-finished materials Matériaux composites Composites Délaminage Delamination Delaminación Effet dimensionnel Size effect Efecto dimensional Fissure Crack Fisura Interface solide solide Solid solid interface Interfase sólido sólido Interphase Interfase Matériau aiguilleté Needled material Material cosado Matériau endommagé Damaged material Material dañado Matériau stratifié Stratified material Material estratificado Modélisation Modeling Modelización Poutre cantilever double Double cantilever beam Viga cantilever doble Poutre épaisse Thick beam Viga espesa Rupture Ruptura Résistance flexion Bending strength Resistencia flexión Ténacité Fracture toughness Tenacidad DCB Laminated composites Mode I Stitching TDCB
Sonstiges:	Nachgewiesen in: PASCAL Archive Sprachen: English Original Material: INIST-CNRS Document Type: Conference Paper File Description: text Language: English Author Affiliations: Electromechanics and Materials Engineering College, Dalian Maritime University, Dalian 116026, China ; School of Aerospace, Mechanical and Mechatronic Engineering, The University of Sydney, NSW2006, Australia Rights: Copyright 2006 INIST-CNRS ; CC BY 4.0 ; Sauf mention contraire ci-dessus, le contenu de cette notice bibliographique peut être utilisé dans le cadre d’une licence CC BY 4.0 Inist-CNRS / Unless otherwise stated above, the content of this bibliographic record may be used under a CC BY 4.0 licence by Inist-CNRS / A menos que se haya señalado antes, el contenido de este registro bibliográfico puede ser utilizado al amparo de una licencia CC BY 4.0 Inist-CNRS Notes: Physics: solid mechanics ; Polymer industry, paints, wood

Klicken Sie ein Format an und speichern Sie dann die Daten oder geben Sie eine Empfänger-Adresse ein und lassen Sie sich per Email zusenden.

BibTeX Citavi, JabRef, u.a.
(Literaturverwaltung)

PDF kein Volltext!
(Merkzettel, Notizen)

RIS Endnote, Citavi u.a.
(Literaturverwaltung)

MODS
(XML zur Weiterverarbeitung)

oder

Wählen Sie das für Sie passende Zitationsformat und kopieren Sie es dann in die Zwischenablage, lassen es sich per Mail zusenden oder speichern es als PDF-Datei.

Gewünschter Zitations-Stil:

oder

Bitte prüfen Sie, ob die Zitation formal korrekt ist, bevor Sie sie in einer Arbeit verwenden. Benutzen Sie gegebenenfalls den "Exportieren"-Dialog, wenn Sie ein Literaturverwaltungsprogramm verwenden und die Zitat-Angaben selbst formatieren wollen.