Bestimmung der interlaminaren Schubfestigkeit zweischichtiger GFK/CFK-Biegeträger in Faserverbundkonstruktion / A determination of interlaminar shear strength for two-layered GFRP/CFRP flexing carriers in a fibre-reinforced composite structure

TAS, Zakir

In: Praktische Metallographie, Jg. 44 (2007), Heft 6, S. 259-272

academicJournal - print, 9 ref

Interlaminar fracture is the way of failure which occurs most frequently in fibre-reinforced composite structures. The reasons which lead to interlaminar fracture are faults in manufacture, damage caused in use, and interlaminar stresses. In case of loads, delaminations appear in fibre-reinforced composites. Interlaminar shear strength is a measure of delamination. This article examines the interlaminar shear strength of multi-layered flexing carriers in a fibre hybrid construction from GFRP and CFRP. The test bars made of GFRP and CFRP were manufactured in two different ways: by integrating manufacture in an autoclaving process and by bonding after an individual manufacture of the composite components. A determination of interlaminar shear strength was made by means of the three-point bending test.

Titel:	Bestimmung der interlaminaren Schubfestigkeit zweischichtiger GFK/CFK-Biegeträger in Faserverbundkonstruktion / A determination of interlaminar shear strength for two-layered GFRP/CFRP flexing carriers in a fibre-reinforced composite structure
Autor/in / Beteiligte Person:	TAS, Zakir
Link:	View record from PASCAL Archive
Zeitschrift:	Praktische Metallographie, Jg. 44 (2007), Heft 6, S. 259-272
Veröffentlichung:	München: Hanser, 2007
Medientyp:	academicJournal
Umfang:	print, 9 ref
ISSN:	0032-678X (print)
Schlagwort:	Metallurgy, welding Métallurgie, soudage Sciences exactes et technologie Exact sciences and technology Physique Physics Domaines interdisciplinaires: science des materiaux; rheologie Cross-disciplinary physics: materials science; rheology Science des matériaux Materials science Diagrammes de phases et microstructures développées par solidification et par transformations de phases solide-solide Phase diagrams and microstructures developed by solidification and solid-solid phase transformations Solidification Sciences appliquees Applied sciences Metaux. Metallurgie Metals. Metallurgy Transformation de matériaux métalliques Production techniques Métallurgie des poudres. Matériaux composites Powder metallurgy. Composite materials Métaux renforcés par des fibres Fibre reinforced metals Cisaillement Shear Matériau composite Composite materials Métal renforcé fibre Fibre reinforced metal Metal reforzado fibra Faserverstaerktes Metall Résistance cisaillement Shear strength Résistance mécanique Mechanical strength
Sonstiges:	Nachgewiesen in: PASCAL Archive Sprachen: German Original Material: INIST-CNRS Document Type: Article File Description: text Language: German Author Affiliations: Gebze Institute of Technology, Engineering Faculty, Gebze - Kocaeli, Turkey Rights: Copyright 2008 INIST-CNRS ; CC BY 4.0 ; Sauf mention contraire ci-dessus, le contenu de cette notice bibliographique peut être utilisé dans le cadre d’une licence CC BY 4.0 Inist-CNRS / Unless otherwise stated above, the content of this bibliographic record may be used under a CC BY 4.0 licence by Inist-CNRS / A menos que se haya señalado antes, el contenido de este registro bibliográfico puede ser utilizado al amparo de una licencia CC BY 4.0 Inist-CNRS Notes: Metals. Metallurgy ; Physics and materials science

Klicken Sie ein Format an und speichern Sie dann die Daten oder geben Sie eine Empfänger-Adresse ein und lassen Sie sich per Email zusenden.

BibTeX Citavi, JabRef, u.a.
(Literaturverwaltung)

PDF kein Volltext!
(Merkzettel, Notizen)

RIS Endnote, Citavi u.a.
(Literaturverwaltung)

MODS
(XML zur Weiterverarbeitung)

oder

Wählen Sie das für Sie passende Zitationsformat und kopieren Sie es dann in die Zwischenablage, lassen es sich per Mail zusenden oder speichern es als PDF-Datei.

Gewünschter Zitations-Stil:

oder

Bitte prüfen Sie, ob die Zitation formal korrekt ist, bevor Sie sie in einer Arbeit verwenden. Benutzen Sie gegebenenfalls den "Exportieren"-Dialog, wenn Sie ein Literaturverwaltungsprogramm verwenden und die Zitat-Angaben selbst formatieren wollen.