The present work was aimed at determining the effect of coating surface condition on the initial corrosion of hot-dip galvanized reinforcing steel bar (HDG rebar) in ordinary Portland cement (OPC) concrete. During zinc corrosion in OPC concrete, calcium hydroxyzincate (CHZ) formed on untreated HDG steel provided sufficient protection against corrosion. Therefore, it is concluded that treating HDG rebar with dilute chromic acid is unnecessary as a method of passivating zinc. A layer of zinc oxide and zinc carbonate formed, through weathering, on HDG bars increased the initial corrosion rate and passivation time compared with the non-weathered rebar exposed to concrete. HDG steel with an alloyed coating, i.e. containing only of Fe-Zn intermetallic phases, required a longer time to passivate than those with a pure zinc surface layer. The lower zinc content of the surface limited the rate of CHZ formation; hence, delayed passivation. Regardless of the surface condition, the coating depth loss after two days of embedment in ordinary Portland cement concrete was insignificant.

Titel:	Effect of surface condition on the initial corrosion of galvanized reinforcing steel embedded in concrete
Autor/in / Beteiligte Person:	TAN, Z. Q ; HANSSON, C. M
Link:	E-Journal im Bestand der UB Hagen? View record from PASCAL Archive
Zeitschrift:	Corrosion science, Jg. 50 (2008), Heft 9, S. 2512-2522
Veröffentlichung:	Kidlington: Elsevier, 2008
Medientyp:	academicJournal
Umfang:	print, 14 ref
ISSN:	0010-938X (print)
Schlagwort:	Metallurgy, welding Métallurgie, soudage Sciences exactes et technologie Exact sciences and technology Sciences appliquees Applied sciences Metaux. Metallurgie Metals. Metallurgy Transformation de matériaux métalliques Production techniques Traitements de surface Surface treatment Dépôt de métaux et d'alliages Metallic coatings Corrosion Action des agents de corrosion Corrosion environments Application Aplicación Anwendung Acier galvanisé Galvanized steel Acero galvanizado Barre à béton Concrete reinforcing bar Barra para hormigón Betonstahl Béton armé Reinforced concrete Hormigón armado Stahlbeton Corrosión Korrosion Etat surface Surface conditions Estado superficie Oberflaechenzustand Revêtement métallique Metal coating Revestimiento metálico Metallischer Ueberzug Spectrométrie Raman Raman spectrometry Espectrometría Raman Traitement surface Tratamiento superficie Oberflaechenbehandlung A. Metal coatings A. Steel reinforced concrete B. Polarization B. Raman spectroscopy C. Alkaline corrosion
Sonstiges:	Nachgewiesen in: PASCAL Archive Sprachen: English Original Material: INIST-CNRS Document Type: Article File Description: text Language: English Author Affiliations: Department of Civil and Environmental Engineering, University of Waterloo, 200 University Avenue West, Waterloo, Ontario, N2L 3G1, Canada Rights: Copyright 2009 INIST-CNRS ; CC BY 4.0 ; Sauf mention contraire ci-dessus, le contenu de cette notice bibliographique peut être utilisé dans le cadre d’une licence CC BY 4.0 Inist-CNRS / Unless otherwise stated above, the content of this bibliographic record may be used under a CC BY 4.0 licence by Inist-CNRS / A menos que se haya señalado antes, el contenido de este registro bibliográfico puede ser utilizado al amparo de una licencia CC BY 4.0 Inist-CNRS Notes: Metals. Metallurgy

Klicken Sie ein Format an und speichern Sie dann die Daten oder geben Sie eine Empfänger-Adresse ein und lassen Sie sich per Email zusenden.

BibTeX Citavi, JabRef, u.a.
(Literaturverwaltung)

PDF kein Volltext!
(Merkzettel, Notizen)

RIS Endnote, Citavi u.a.
(Literaturverwaltung)

MODS
(XML zur Weiterverarbeitung)

oder

Wählen Sie das für Sie passende Zitationsformat und kopieren Sie es dann in die Zwischenablage, lassen es sich per Mail zusenden oder speichern es als PDF-Datei.

Gewünschter Zitations-Stil:

oder

Bitte prüfen Sie, ob die Zitation formal korrekt ist, bevor Sie sie in einer Arbeit verwenden. Benutzen Sie gegebenenfalls den "Exportieren"-Dialog, wenn Sie ein Literaturverwaltungsprogramm verwenden und die Zitat-Angaben selbst formatieren wollen.

Effect of surface condition on the initial corrosion of galvanized reinforcing steel embedded in concrete