Characterisation of residual stress and interface degradation in TBCs by photo-luminescence piezo-spectroscopy

WANG, X ; WU, R. T ; et al.

In: Surface & coatings technology, Jg. 204 (2010), Heft 15, S. 2472-2482

academicJournal - print, 30 ref

Residual stress in the TGO in two different TBC systems, one with a Pt aluminide (β structure) bond coat and another with a Pt diffusion (γγ' structure) bond coat, were studied using photo-luminescence piezospectroscopy (PLPS). The luminescence spectra and TGO morphology were investigated progressively with thermal cycling at 1135 °C. The two TBC systems were found to have distinctly different TGO residual stresses and different failure modes. Several stress relaxation mechanisms were found to be operative in the Pt aluminide system, while no stress relaxation was evident in the Pt diffusion system until close to the end of life (spallation). Luminescence spectral shape evolution has been quantitatively analysed and correlated with TBC system degradation processes. Both TBC systems showed clear spectral shape changes as a result of the formation of interface cracks when they reached approximately 75% lifetime. Characteristic spectral shape changes in response to different types of interface crack were demonstrated experimentally. The correlation between spectral shape evolution and interface degradation opens a new avenue for studies of degradation and lifetime assessment of TBCs.

Titel:	Characterisation of residual stress and interface degradation in TBCs by photo-luminescence piezo-spectroscopy
Autor/in / Beteiligte Person:	WANG, X ; WU, R. T ; ATKINSON, A
Link:	E-Journal im Bestand der UB Hagen? View record from PASCAL Archive
Zeitschrift:	Surface & coatings technology, Jg. 204 (2010), Heft 15, S. 2472-2482
Veröffentlichung:	Amsterdam: Elsevier, 2010
Medientyp:	academicJournal
Umfang:	print, 30 ref
ISSN:	0257-8972 (print)
Schlagwort:	General chemistry, physical chemistry Chimie générale, chimie physique Metallurgy, welding Métallurgie, soudage Sciences exactes et technologie Exact sciences and technology Physique Physics Domaines interdisciplinaires: science des materiaux; rheologie Cross-disciplinary physics: materials science; rheology Science des matériaux Materials science Traitements de surface Surface treatments Sciences appliquees Applied sciences Metaux. Metallurgie Metals. Metallurgy Transformation de matériaux métalliques Production techniques Surface treatment Dépôt de matériaux non métalliques Nonmetallic coatings Barrière thermique Thermal barriers Contrainte résiduelle Residual stresses Interface Interfaces Revêtement non métallique Non metal coating Revestimiento no metálico Nichtmetallischer Ueberzug Traitement surface Interface degradation Luminescence spectroscopy Residual stress Spectral shape TBCs
Sonstiges:	Nachgewiesen in: PASCAL Archive Sprachen: English Original Material: INIST-CNRS Document Type: Article File Description: text Language: English Author Affiliations: Department of Materials, Imperial College London, London SW7 2AZ, United Kingdom Rights: Copyright 2015 INIST-CNRS ; CC BY 4.0 ; Sauf mention contraire ci-dessus, le contenu de cette notice bibliographique peut être utilisé dans le cadre d’une licence CC BY 4.0 Inist-CNRS / Unless otherwise stated above, the content of this bibliographic record may be used under a CC BY 4.0 licence by Inist-CNRS / A menos que se haya señalado antes, el contenido de este registro bibliográfico puede ser utilizado al amparo de una licencia CC BY 4.0 Inist-CNRS Notes: Metals. Metallurgy ; Physics and materials science

Klicken Sie ein Format an und speichern Sie dann die Daten oder geben Sie eine Empfänger-Adresse ein und lassen Sie sich per Email zusenden.

BibTeX Citavi, JabRef, u.a.
(Literaturverwaltung)

PDF kein Volltext!
(Merkzettel, Notizen)

RIS Endnote, Citavi u.a.
(Literaturverwaltung)

MODS
(XML zur Weiterverarbeitung)

oder

Wählen Sie das für Sie passende Zitationsformat und kopieren Sie es dann in die Zwischenablage, lassen es sich per Mail zusenden oder speichern es als PDF-Datei.

Gewünschter Zitations-Stil:

oder

Bitte prüfen Sie, ob die Zitation formal korrekt ist, bevor Sie sie in einer Arbeit verwenden. Benutzen Sie gegebenenfalls den "Exportieren"-Dialog, wenn Sie ein Literaturverwaltungsprogramm verwenden und die Zitat-Angaben selbst formatieren wollen.