Microstructure characteristics and mechanical property of aluminum alloy/stainless steel lap joints fabricated by MIG welding―brazing process

HONGTAO, ZHANG ; JIAKUN, LIU

In: Materials science & engineering. A, Structural materials : properties, microstructure and processing, Jg. 528 (2011), Heft 19-20, S. 6179-6185

academicJournal - print, 17 ref

Wie komme ich dran?

Lap joints of aluminum alloy 2B50 and stainless steel 1Cr18Ni9Ti were welded by MIG welding-brazing method with 4043 Al―Si filler metal. The effect of aluminizing coating and galvanized zinc coating on fusion metal spreadability were studied. The aluminized coating had limited effect to promote weld surface appearance and obvious micro-cracks were found between the compound layer and the steel side. The fracture in tensile tests occurred at the interfacial layer of the weld with a low tensile strength about 60 MPa. Joints between aluminum alloy and galvanized steel had good surface appearances and the intermetallic compound in fusion zone region close to joint interface was Al4.5FeSi. The thickness of the intermetallic compound layer varied from about 5 μm to 15 μm depending on the heat input and the highest tensile strength of lap joint could reached 193.6 MPa when the heat input is 0.846 KJ/cm.

Titel:	Microstructure characteristics and mechanical property of aluminum alloy/stainless steel lap joints fabricated by MIG welding―brazing process
Autor/in / Beteiligte Person:	HONGTAO, ZHANG ; JIAKUN, LIU
Link:	E-Journal im Bestand der UB Hagen? View record from PASCAL Archive
Zeitschrift:	Materials science & engineering. A, Structural materials : properties, microstructure and processing, Jg. 528 (2011), Heft 19-20, S. 6179-6185
Veröffentlichung:	Kidlington: Elsevier, 2011
Medientyp:	academicJournal
Umfang:	print, 17 ref
ISSN:	0921-5093 (print)
Schlagwort:	Crystallography Cristallographie cristallogenèse Chemical industry parachemical industry Industrie chimique et parachimique Metallurgy, welding Métallurgie, soudage Condensed state physics Physique de l'état condensé Sciences exactes et technologie Exact sciences and technology Sciences appliquees Applied sciences Metaux. Metallurgie Metals. Metallurgy Assemblage et découpage thermique: aspects métallurgiques Joining, thermal cutting: metallurgical aspects Soudage Welding Propriétés mécaniques. Rhéologie. Mécanique de la rupture. Tribologie Mechanical properties and methods of testing. Rheology. Fracture mechanics. Tribology Rupture Fractures Acier galvanisé Galvanized steel Acero galvanizado Acier inoxydable Stainless steel Acero inoxidable Nichtrostender Stahl Alliage base aluminium Aluminium base alloys Aluminisation Aluminizing Aluminizacion Aluminieren Diffraction électron sélection aire SAED Essai traction Tension test Ensayo tracción Zugversuch Joint recouvrement Lap joint Junta recubierta Microscopie électronique transmission Transmission electron microscopy Microscopía electrónica transmisión Transmissionselektronenmikroskopie Microstructure Microestructura Mikrogefuege Métal transition Transition metal Metal transición Uebergangsmetalle Propriété mécanique Mechanical properties Propiedad mecánica Ruptura Bruch Résistance traction Tensile strength Resistencia tracción Zugfestigkeit Soudage MIG MIG welding Soldeo MIG MIG Schweissen Aluminum Mechanical property Steel Welding-brazing
Sonstiges:	Nachgewiesen in: PASCAL Archive Sprachen: English Original Material: INIST-CNRS Document Type: Article File Description: text Language: English Author Affiliations: School of Materials Science and Engineering, Harbin Institute of Technology at Weihai, Weihai 264209, China Rights: Copyright 2015 INIST-CNRS ; CC BY 4.0 ; Sauf mention contraire ci-dessus, le contenu de cette notice bibliographique peut être utilisé dans le cadre d’une licence CC BY 4.0 Inist-CNRS / Unless otherwise stated above, the content of this bibliographic record may be used under a CC BY 4.0 licence by Inist-CNRS / A menos que se haya señalado antes, el contenido de este registro bibliográfico puede ser utilizado al amparo de una licencia CC BY 4.0 Inist-CNRS Notes: Metals. Metallurgy

Klicken Sie ein Format an und speichern Sie dann die Daten oder geben Sie eine Empfänger-Adresse ein und lassen Sie sich per Email zusenden.

BibTeX Citavi, JabRef, u.a.
(Literaturverwaltung)

PDF kein Volltext!
(Merkzettel, Notizen)

RIS Endnote, Citavi u.a.
(Literaturverwaltung)

MODS
(XML zur Weiterverarbeitung)

oder

Wählen Sie das für Sie passende Zitationsformat und kopieren Sie es dann in die Zwischenablage, lassen es sich per Mail zusenden oder speichern es als PDF-Datei.

Gewünschter Zitations-Stil:

oder

Bitte prüfen Sie, ob die Zitation formal korrekt ist, bevor Sie sie in einer Arbeit verwenden. Benutzen Sie gegebenenfalls den "Exportieren"-Dialog, wenn Sie ein Literaturverwaltungsprogramm verwenden und die Zitat-Angaben selbst formatieren wollen.