Effect of stacking sequence on R-curve behavior of glass/epoxy DCB laminates with 0°//0° crack interface

SHOKRIEH, M. M ; HEIDARI-RARANI, M

In: Materials science & engineering. A, Structural materials : properties, microstructure and processing, Jg. 529C (2011), S. 265-269

academicJournal - print, 20 ref

Wie komme ich dran?

In this study, the influence of stacking sequence on mode I delamination resistance (R-curve) behavior of E-glass/epoxy laminated composites with an initial delamination between 0°//0° interface is experimentally investigated. To this end, symmetric double cantilever beam (DCB) specimens of stacking sequences; [0°12]s,[(0°/90°)3]2s and [0°/90°/± 45°/90°/0°]2s with two initial crack lengths are used. A pronounced R-curve behavior is observed on all stacking sequences due to locating delamination between two similar layers. Comparison of R-curve behavior of cross-ply and quasi-isotropic DCB specimens with unidirectional (UD) one reveals the significant effect of the non-dimensional coupling parameter, Dc = D212/D11D22, on the R-curves. Thus, three main outputs of R-curves could be summarized as; (a) the initiation delamination toughness G1c-init) of multidirectional (MD) laminates are much lower than that of UD one, (b) stacking sequence has no effect on the fiber bridging length in DCB specimens, and (c) the greater the Dc value of a laminate, the higher the steady-state propagation toughness (G1c-prop) is.

Titel:	Effect of stacking sequence on R-curve behavior of glass/epoxy DCB laminates with 0°//0° crack interface
Autor/in / Beteiligte Person:	SHOKRIEH, M. M ; HEIDARI-RARANI, M
Link:	E-Journal im Bestand der UB Hagen? View record from PASCAL Archive
Zeitschrift:	Materials science & engineering. A, Structural materials : properties, microstructure and processing, Jg. 529C (2011), S. 265-269
Veröffentlichung:	Kidlington: Elsevier, 2011
Medientyp:	academicJournal
Umfang:	print, 20 ref
ISSN:	0921-5093 (print)
Schlagwort:	Crystallography Cristallographie cristallogenèse Chemical industry parachemical industry Industrie chimique et parachimique Metallurgy, welding Métallurgie, soudage Condensed state physics Physique de l'état condensé Sciences exactes et technologie Exact sciences and technology Sciences appliquees Applied sciences Industrie des polymeres, peintures, bois Polymer industry, paints, wood Technologie des polymères Technology of polymers Propriétés et essais Properties and testing Propriétés physiques Physical properties Propriétés mécaniques Mechanical properties Formes d'application et semiproduits Forms of application and semi-finished materials Stratifiés Laminates Dispositif expérimental Experimental device Dispositivo experimental Délaminage Delamination Delaminación Déplacement déformation Displacement(deformation) Desplazamiento deformación Epoxyde résine Epoxy resin Epóxido resina Fissure interface Interface crack Fisura interfase Longueur fissure Crack length Largo fisura Matériau composite Composite material Material compuesto Mode empilement Stacking sequence Modo apilamiento Méthode essai Test method Método ensayo Résistance propagation fissure Crack propagation resistance Resistencia propagación grieta Stratifié Laminate Estratificado Ténacité Fracture toughness Tenacidad Verre Glass Vidrio Delamination toughness Multidirectional DCB R-curve
Sonstiges:	Nachgewiesen in: PASCAL Archive Sprachen: English Original Material: INIST-CNRS Document Type: Article File Description: text Language: English Author Affiliations: Composites Research Laboratory, Center of Excellence in Experimental Solid Mechanics and Dynamics, School of Mechanical Engineering, Iran University of Science and Technology (IUST), Tehran 16846-13114, Iran, Islamic Republic of Rights: Copyright 2015 INIST-CNRS ; CC BY 4.0 ; Sauf mention contraire ci-dessus, le contenu de cette notice bibliographique peut être utilisé dans le cadre d’une licence CC BY 4.0 Inist-CNRS / Unless otherwise stated above, the content of this bibliographic record may be used under a CC BY 4.0 licence by Inist-CNRS / A menos que se haya señalado antes, el contenido de este registro bibliográfico puede ser utilizado al amparo de una licencia CC BY 4.0 Inist-CNRS Notes: Polymer industry, paints, wood

Klicken Sie ein Format an und speichern Sie dann die Daten oder geben Sie eine Empfänger-Adresse ein und lassen Sie sich per Email zusenden.

BibTeX Citavi, JabRef, u.a.
(Literaturverwaltung)

PDF kein Volltext!
(Merkzettel, Notizen)

RIS Endnote, Citavi u.a.
(Literaturverwaltung)

MODS
(XML zur Weiterverarbeitung)

oder

Wählen Sie das für Sie passende Zitationsformat und kopieren Sie es dann in die Zwischenablage, lassen es sich per Mail zusenden oder speichern es als PDF-Datei.

Gewünschter Zitations-Stil:

oder

Bitte prüfen Sie, ob die Zitation formal korrekt ist, bevor Sie sie in einer Arbeit verwenden. Benutzen Sie gegebenenfalls den "Exportieren"-Dialog, wenn Sie ein Literaturverwaltungsprogramm verwenden und die Zitat-Angaben selbst formatieren wollen.