Carbon-fibre epoxy prepreg (CFC) curing in an autoclave analogue process controlled by Dynamic Mechanical Analysis (DMA)

STARK, W ; JAUNICH, M ; et al.

In: Polymer testing, Jg. 32 (2013), Heft 8, S. 1487-1494

Online academicJournal - print, 56 ref

Zugriff:

Full Text Finder (Volltext)

Carbon fibre prepregs have found widespread application in lightweight constructions. They are based on a carbon-fibre fabric impregnated with reactive epoxy resin. DMA measurements under temperature conditions similar to an autoclave programme were carried out using commercially available prepreg material with a high glass transition temperature. The characteristic of the temperature programme was a dynamic heating segment at 1.5 K/min followed by a longer isothermal segment at 180 °C. The courses of the storage modulus Eʹ, loss modulus E and tanδ were recorded. The measuring frequency was varied between 1 Hz and 33.3 Hz. Gelation and vitrification are assigned. The influence of the measuring frequency on the time to vitrification and the correlation with DSC are discussed. The reaction does not end even after 10 h curing at 180°C, which is interpreted as the slow cessation of the reaction caused by vitrification.

Titel:	Carbon-fibre epoxy prepreg (CFC) curing in an autoclave analogue process controlled by Dynamic Mechanical Analysis (DMA)
Autor/in / Beteiligte Person:	STARK, W ; JAUNICH, M ; MCHUGH, J
Link:	Full Text Finder (Volltext) E-Journal im Bestand der UB Hagen? View record from PASCAL Archive
Zeitschrift:	Polymer testing, Jg. 32 (2013), Heft 8, S. 1487-1494
Veröffentlichung:	Kindlington: Elsevier, 2013
Medientyp:	academicJournal
Umfang:	print, 56 ref
ISSN:	0142-9418 (print)
Schlagwort:	Polymers, paint and wood industries Polymères, industries des peintures et bois Sciences exactes et technologie Exact sciences and technology Sciences appliquees Applied sciences Industrie des polymeres, peintures, bois Polymer industry, paints, wood Technologie des polymères Technology of polymers Formes d'application et semiproduits Forms of application and semi-finished materials Stratifiés Laminates Autoclave Durcissement (matière plastique) Curing (plastics) Endurecimiento (material plástico) Effet température Temperature effect Efecto temperatura Epoxyde résine Epoxy resin Epóxido resina Etude expérimentale Experimental study Estudio experimental Fibre carbone Carbon fiber Fibra carbón Fibre minérale Mineral fiber Fibra inorgánica Gélification Gelation Gelificación Matériau composite Composite material Material compuesto Matériau renforcé fibre Fiber reinforced material Material reforzado fibra Module conservation Storage modulus Módulo conservación Module perte Loss modulus Módulo pérdida Propriété dynamomécanique Dynamic mechanical properties Propiedad dinamomecánica Propriété rhéologique Rheological properties Propiedad reológica Propriété thermique Thermal properties Propiedad térmica Stratifié Laminate Estratificado Tissu textile Woven material Tela textil Vitrification Vitrificación Tissu carbone CFC Curing DMA DSC Glass transition Prepreg
Sonstiges:	Nachgewiesen in: PASCAL Archive Sprachen: English Original Material: INIST-CNRS Document Type: Article File Description: text Language: English Author Affiliations: BAM Federal Institute for Materials Research and Testing, Unter den Eichen 87, 12205 Berlin, Germany ; BMW Group, Landshut, Germany Rights: Copyright 2015 INIST-CNRS ; CC BY 4.0 ; Sauf mention contraire ci-dessus, le contenu de cette notice bibliographique peut être utilisé dans le cadre d’une licence CC BY 4.0 Inist-CNRS / Unless otherwise stated above, the content of this bibliographic record may be used under a CC BY 4.0 licence by Inist-CNRS / A menos que se haya señalado antes, el contenido de este registro bibliográfico puede ser utilizado al amparo de una licencia CC BY 4.0 Inist-CNRS Notes: Polymer industry, paints, wood

Klicken Sie ein Format an und speichern Sie dann die Daten oder geben Sie eine Empfänger-Adresse ein und lassen Sie sich per Email zusenden.

BibTeX Citavi, JabRef, u.a.
(Literaturverwaltung)

PDF kein Volltext!
(Merkzettel, Notizen)

RIS Endnote, Citavi u.a.
(Literaturverwaltung)

MODS
(XML zur Weiterverarbeitung)

oder

Wählen Sie das für Sie passende Zitationsformat und kopieren Sie es dann in die Zwischenablage, lassen es sich per Mail zusenden oder speichern es als PDF-Datei.

Gewünschter Zitations-Stil:

oder

Bitte prüfen Sie, ob die Zitation formal korrekt ist, bevor Sie sie in einer Arbeit verwenden. Benutzen Sie gegebenenfalls den "Exportieren"-Dialog, wenn Sie ein Literaturverwaltungsprogramm verwenden und die Zitat-Angaben selbst formatieren wollen.