Double cantilever beam (DCB) specimens fabricated from a graphite/epoxy (G0814/913) woven prepreg containing a straight through notch were tested by means of constant amplitude fatigue. The specimen was composed of 15 layers with fibers alternating between the weft and warp in the 0°/90° and the +45°/-45° directions. Eight fatigue tests were carried out to determine the delamination growth rate da/dN vs the nearly mode I cyclic energy release rate ΔG1. Comparison of the delamination growth rate was made to the crack propagation rate of an aluminum alloy. It was found that a crack in the aluminum will grow faster but will be less sensitive to uncertainties or changes in load level.

Titel:	Delamination propagation in a multi-directional woven composite DCB specimen subjected to fatigue loading
Autor/in / Beteiligte Person:	ISHBIR, Chaim ; BANKS-SILLS, Leslie ; FOURMAN, Victor ; ELIASI, Rami
Link:	E-Journal im Bestand der UB Hagen? View record from PASCAL Archive
Zeitschrift:	Composites. Part B, Engineering, Jg. 66 (2014), S. 180-189
Veröffentlichung:	Kidlington: Elsevier, 2014
Medientyp:	academicJournal
Umfang:	print, 23 ref
ISSN:	1359-8368 (print)
Schlagwort:	Chemical industry parachemical industry Industrie chimique et parachimique Mechanics acoustics Mécanique et acoustique Metallurgy, welding Métallurgie, soudage Polymers, paint and wood industries Polymères, industries des peintures et bois Sciences exactes et technologie Exact sciences and technology Sciences appliquees Applied sciences Industrie des polymeres, peintures, bois Polymer industry, paints, wood Technologie des polymères Technology of polymers Formes d'application et semiproduits Forms of application and semi-finished materials Stratifiés Laminates Aluminium alliage Aluminium alloy Aluminio aleación Délaminage Delamination Delaminación Effet entaille Notch sensitivity Sensibilidad entalladura Epoxyde résine Epoxy resin Epóxido resina Essai fatigue Fatigue test Ensayo fatiga Etude expérimentale Experimental study Estudio experimental Fibre carbone Carbon fiber Fibra carbón Fibre minérale Mineral fiber Fibra inorgánica Matériau composite Composite material Material compuesto Matériau renforcé fibre Fiber reinforced material Material reforzado fibra Norme ASTM ASTM standard Norma ASTM Poutre cantilever double Double cantilever beam Viga cantilever doble Propriété mécanique Mechanical properties Propiedad mecánica Résistance fatigue Fatigue strength Resistencia fatiga Résistance propagation fissure Crack propagation resistance Resistencia propagación grieta Stratifié Laminate Estratificado Tissu textile Woven material Tela textil Matériau fibre multidirectionnelle Tissu carbone A. Fabrics/textiles A. carbon fiber B. Delamination B. Fatigue
Sonstiges:	Nachgewiesen in: PASCAL Archive Sprachen: English Original Material: INIST-CNRS Document Type: Article File Description: text Language: English Author Affiliations: Dreszer Fracture Mechanics Laboratory, School of Mechanical Engineering, Tel Aviv University, Ramat Aviv 69978, Israel Rights: Copyright 2015 INIST-CNRS ; CC BY 4.0 ; Sauf mention contraire ci-dessus, le contenu de cette notice bibliographique peut être utilisé dans le cadre d’une licence CC BY 4.0 Inist-CNRS / Unless otherwise stated above, the content of this bibliographic record may be used under a CC BY 4.0 licence by Inist-CNRS / A menos que se haya señalado antes, el contenido de este registro bibliográfico puede ser utilizado al amparo de una licencia CC BY 4.0 Inist-CNRS Notes: Polymer industry, paints, wood

Klicken Sie ein Format an und speichern Sie dann die Daten oder geben Sie eine Empfänger-Adresse ein und lassen Sie sich per Email zusenden.

BibTeX Citavi, JabRef, u.a.
(Literaturverwaltung)

PDF kein Volltext!
(Merkzettel, Notizen)

RIS Endnote, Citavi u.a.
(Literaturverwaltung)

MODS
(XML zur Weiterverarbeitung)

oder

Wählen Sie das für Sie passende Zitationsformat und kopieren Sie es dann in die Zwischenablage, lassen es sich per Mail zusenden oder speichern es als PDF-Datei.

Gewünschter Zitations-Stil:

oder

Bitte prüfen Sie, ob die Zitation formal korrekt ist, bevor Sie sie in einer Arbeit verwenden. Benutzen Sie gegebenenfalls den "Exportieren"-Dialog, wenn Sie ein Literaturverwaltungsprogramm verwenden und die Zitat-Angaben selbst formatieren wollen.

Delamination propagation in a multi-directional woven composite DCB specimen subjected to fatigue loading