Tension―tension fatigue properties of SiC fiber reinforced Ti―6Al―4V matrix composite (SiCf/Ti―6Al―4V) at room temperature were investigated. Fatigue tests were conducted under a load-controlled mode with a stress ratio 0.1 and a frequency 10 Hz under a maximum applied stress ranging from 600 to 1200 MPa. The relationship between the applied stress and fatigue life was determined and fracture surfaces were examined to study the fatigue damage and fracture failure mechanisms using SEM. The results show that, the fatigue life of the SiCf/Ti―6Al―4V composite decreases substantially in proportion to the increase in maximum applied stress. Moreover, in the medium and high life range, the relationship between the maximum applied stress and cycles to failure in the semi-logarithmic system could be fitted as a linear equation: Smax/μ = 1.381 ― 0.152 × IgNf. Fractographic analysis revealed that fatigue fracture surfaces consist of a fatigued region and a fast fracture region. The fraction of the fatigued region with respect to the total fracture surface decreases with the increase of the applied maximum stresses.

Titel:	Fatigue properties and fracture analysis of a SiC fiber-reinforced titanium matrix composite
Autor/in / Beteiligte Person:	FENG, G. H ; YANG, Y. Q ; LUO, X ; LI, J ; HUANG, B ; CHEN, Y
Link:	E-Journal im Bestand der UB Hagen? View record from PASCAL Archive
Zeitschrift:	Composites. Part B, Engineering, Jg. 68 (2014), S. 336-342
Veröffentlichung:	Kidlington: Elsevier, 2014
Medientyp:	academicJournal
Umfang:	print, 36 ref
ISSN:	1359-8368 (print)
Schlagwort:	Chemical industry parachemical industry Industrie chimique et parachimique Mechanics acoustics Mécanique et acoustique Metallurgy, welding Métallurgie, soudage Polymers, paint and wood industries Polymères, industries des peintures et bois Sciences exactes et technologie Exact sciences and technology Sciences appliquees Applied sciences Metaux. Metallurgie Metals. Metallurgy Transformation de matériaux métalliques Production techniques Métallurgie des poudres. Matériaux composites Powder metallurgy. Composite materials Métaux renforcés par des fibres Fibre reinforced metals Carbure de silicium Silicon carbide Silicio carburo Siliciumcarbid Composite matrice métallique Metal matrix composite Compuesto matriz metalico Céramique sans oxyde Non oxide ceramics Cerámica sin óxido Diagramme SN SN diagram Diagrama SN Woehler Kurve Durée vie fatigue Fatigue life Longevidad fatiga Ermuedungslebensdauer Etude expérimentale Experimental study Estudio experimental Experimentelle Untersuchung Fibre céramique Ceramic fiber Fibra cerámica Keramikfaser Fibre minérale Mineral fiber Fibra inorgánica Matériau composite Composite material Material compuesto Verbundwerkstoff Mode rupture Fracture mode Modo ruptura Métal renforcé fibre Fibre reinforced metal Metal reforzado fibra Faserverstaerktes Metall Propriété mécanique Mechanical properties Propiedad mecánica Propriété traction Tensile property Propiedad tracción Zugeigenschaft Résistance fatigue Fatigue strength Resistencia fatiga Dauerfestigkeit Titane alliage Titanium alloy Titanio aleación Titanlegierung A. Fibers A. Metal-matrix composites (MMCs) B. Fatigue D. Fractography
Sonstiges:	Nachgewiesen in: PASCAL Archive Sprachen: English Original Material: INIST-CNRS Document Type: Article File Description: text Language: English Author Affiliations: State Key Lab of Solidification Processing, Northwestern Polytechnical University, Xi'an 710072, China Rights: Copyright 2015 INIST-CNRS ; CC BY 4.0 ; Sauf mention contraire ci-dessus, le contenu de cette notice bibliographique peut être utilisé dans le cadre d’une licence CC BY 4.0 Inist-CNRS / Unless otherwise stated above, the content of this bibliographic record may be used under a CC BY 4.0 licence by Inist-CNRS / A menos que se haya señalado antes, el contenido de este registro bibliográfico puede ser utilizado al amparo de una licencia CC BY 4.0 Inist-CNRS Notes: Metals. Metallurgy

Klicken Sie ein Format an und speichern Sie dann die Daten oder geben Sie eine Empfänger-Adresse ein und lassen Sie sich per Email zusenden.

BibTeX Citavi, JabRef, u.a.
(Literaturverwaltung)

PDF kein Volltext!
(Merkzettel, Notizen)

RIS Endnote, Citavi u.a.
(Literaturverwaltung)

MODS
(XML zur Weiterverarbeitung)

oder

Wählen Sie das für Sie passende Zitationsformat und kopieren Sie es dann in die Zwischenablage, lassen es sich per Mail zusenden oder speichern es als PDF-Datei.

Gewünschter Zitations-Stil:

oder

Bitte prüfen Sie, ob die Zitation formal korrekt ist, bevor Sie sie in einer Arbeit verwenden. Benutzen Sie gegebenenfalls den "Exportieren"-Dialog, wenn Sie ein Literaturverwaltungsprogramm verwenden und die Zitat-Angaben selbst formatieren wollen.

Fatigue properties and fracture analysis of a SiC fiber-reinforced titanium matrix composite