The present work aimed to prepare novel bio-based composites by adding fillers coming from agro-wastes to an acrylate epoxidized soybean oil (AESO) resin, using liquid crystal display (LCD) 3D printing. Different photocurable formulations were prepared by varying the reactive diluents, iso-bornyl methacrylate (IBOMA) and tetrahydrofurfuryl acrylate (THFA). Then, two fillers derived from different industrial wastes, corn (GTF) and wine (WPL-CF) by-products, were added to the AESO-based formulations to develop polymer composites with improved properties. The printability by LCD of the photocurable formulations was widely studied. Bio-based objects with different geometries were realized, showing printing accuracy, layer adhesion, and accurate details. The thermo-mechanical and mechanical properties of the 3D-printed composites were tested by TGA, DMA, and tensile tests. The results revealed that the agro-wastes' addition led to a remarkable increase in the elastic modulus, tensile strength, and glass transition temperature in the glassy state for the systems containing IBOMA and for flexible structures in the rubbery region for systems containing THFA. AESO-based polymers demonstrated tunable properties, varying from rigid to flexible, in the presence of different diluents and biofillers. This finding paves the way for the use of this kind of composite in applications, such as biomedical for the realization of prostheses.
Keywords: bio-based polymer composites; acrylate epoxidized soybean oil; 3D printing; liquid crystal display; biofillers
Recently, several 3D-printing processes for polymers have been commercially introduced to the market, and a growing number of 3D printers for academic, industrial, and home use are extending the use of additive manufacturing (AM) processes, as consumers can design objects based on their desires [[
Although the literature presents a wide collection of studies on 3D-printed polymer composites, the addition of bio-based fillers derived from agro-wastes to soybean oil resin for the realization of composites by LCD [[
For this reason, the aim of the present research highlights the realization of biodegradable soybean oil-based parts by using LCD as a 3D-printing technique.
This paper aims to combine the advantages of bio-based composites prepared by valorizing biofillers coming from agricultural industry wastes and the advantages of 3D-printing vat photopolymerization. It focuses attention on the preparation and characterization of polymer composites by using a relatively new VP technique like LCD, which gives rise to the realization of 3D-printed components with a higher print quality and accuracy with respect to DLP 3D printing. This can prevalently be due to the density of pixels of the LCD screen resolution, which offers the opportunity to print larger components with no difference in terms of quality from smaller models [[
For this reason, two bio-based monofunctional diluents, iso-bornyl methacrylate (IBOMA) and tetrahydrofurfuryl acrylate (THFA), were firstly added to AESO resin in order to tune its viscosity and increase its flowability. The formulations were polymerized by an LCD 3D printer to obtain samples as references. Then, AESO-based composites were prepared by dispersing two different kinds of fillers coming from industrial wastes within the photocurable matrix to enhance its final properties.
Acrylate epoxidized soybean oil (AESO) was used as a bio-based starting photocurable resin. It is as a viscous yellow liquid, with a density of 1.04 g/mL at 25 °C. Two different bio-based diluents were employed to prepare the polymeric photocurable formulations: iso-bornyl methacrylate (IBOMA), coming from pine trees with a density of 0.983 g/mL at 25 °C, and tetrahydrofurfuryl acrylate (THFA) with a density of 1.064 g/mL at 25 °C. Phenyl bis (2,4,6-trimethylbenzoyl) phosphine oxide (BAPO) was chosen as a radical photoinitiator. All the chemicals for the formulations were purchased from Merck (Merck KGaA, Darmstadt, Germany.
Two different biofillers coming from agro-wastes were added to the photocurable formulations: a yellow natural filler derived from maize by-products, named GTF, and a purple powder obtained by pressing grape solid residues obtained from wine production, named WPL-CF, kindly supplied by Agromateriae srl (Faenza, RA, Italy).
Several photocurable formulations were firstly prepared by mixing the acrylate epoxidized soybean oil resin (AESO) with different weight percentages of the two selected bio-based diluents, IBOMA and THFA, in a range between 20 to 50 wt.%, in the presence of BAPO as a photoinitiator for each formulation.
The prepared photocurable formulations were then tested in terms of viscosity and flowability to determine the best compromise between AESO resin viscosity and the diluent capacity of IBOMA or THFA, which can guarantee good final printability for LCD 3D-printing processing.
After the preliminary tests, once the best AESO-based formulation in terms of viscosity and processability had been identified, the formulations containing 60 wt.% of AESO and 40 wt.% of IBOMA or THFA were selected. Subsequently, bio-based composites were prepared by adding 2 parts per hundred resin (phr) of BAPO as a photoinitiator and 5 phr of the two biofillers (GTF and WPL-CF) derived from agricultural wastes to the liquid photocurable formulations.
The dispersion of the fillers was carried out by combining 30 min of magnetic stirring and 15 min of an ultrasonic bath for a total of 4 h to promote a faster dispersion of the powders within the photocurable mixture containing AESO resin and diluents. This procedure made the process less time-consuming and avoided the formation of air bubbles, which can have negative effects on the following printing process.
AESO-based formulations were 3D printed by using a Phrozen Sonic Mini 8K (Phrozen, Hsinchu City, Taiwan) vat photopolymerization 3D printer, LCD type. This printer is characterized by a Linear Projection LED Module, which has an xy resolution of 22 μm, while it has a z resolution or layer thickness e between 0.01 and 0.30 mm and a printing volume of 16.5 (l) × 7.2 (w) × 18 (h) cm
The LCD 3D printing machine is also equipped with a slicer software, called CHITUBOX V1.9.0, which permits the STL file of the desired part to be loaded, the orientation of the piece to be chosen, and, eventually, for supports that can connect the piece to the printing platform to be applied. The program also allows us to modify the printing parameters, like layer thickness, exposure time, and speed, during the printing process.
Firstly, the printability of each AESO-based formulation was studied, and the corresponding printing parameters were optimized for the preparation of the composite formulations. The 3D-printed samples, removed from the platform, were washed in iso-propyl alcohol (Merck) and post-cured for 30 min with an Anycubic Wash & Cure Plus machine (Anycubic Technology Co, Hongkong).
The viscosity of AESO-based liquid formulations containing the two different diluents was measured at 25 °C by using an Anton Paar MCR 702e MultiDrive Rheometer (Graz, Austria) in a parallel plate configuration and in the shear range of 10–104 L/s.
The insoluble fraction, also known as gel content, of rectangular photocured samples was determined by measuring the weight loss of each sample after 24 h of extraction with chloroform at room temperature, according to the ASTM D2765-84 technical standard.
The morphology of the specimens was investigated by a Phenom™ XL Scanning Electron Microscope (Thermo Fisher Scientific, Waltham, MA, USA) at a voltage of 10 kV. The samples were previously metallized with platinum for 15 s using a Quorum Sputter Coater, Q150T S (Laughton, East Sussex, UK). Each specimen was fractured in liquid nitrogen and the fracture surface was analyzed.
Thermogravimetric (TG) analysis was performed by using a Mettler-Toledo TGA 851e instrument (Columbus, OH, USA). All the 3D-printed samples were heated from 25 up to 900 °C at a heating rate of 10 °C/min in air. The TG curves were normalized to the mass of each sample, and the DTG curves were calculated on their relative thermograms.
The dynamic mechanical analysis (DMTA) was carried out from 0 to 200 °C by using an Anton Paar MCR 702e Multi Drive Rheometer (Graz, Austria) at a frequency of 1 Hz in tensile configuration. The samples tested were rectangular with a length (l) of 50 mm, a width (w) of 10 mm, and a thickness (t) of 2 mm.
The mechanical properties of the 3D-printed sample, such as Young's modulus, tensile strength, and elongation at break, were investigated by tensile tests according to ASTM D638-14, using an Instron 5966 equipped with a 2 kN load cell and pneumatic grips, with a deformation rate of 5 mm/min and a grip separation of 50 mm. Deformation was calculated using a displacement transducer. The specimens were type 5 and dog bone-shaped, with gauge lengths of 26 mm, widths of 4 mm, and thicknesses of 2 mm.
The two biofillers coming from agro-wastes were characterized from morphological and thermal points of view. SEM images, reported in Figure 1, were firstly acquired to examine the morphology of the GTF (a) and WPL-CF (b) fillers, which are characterized by the typical structure of milled materials with average dimensions between 20 and 40 µm. GTF powder has tiny flake particles, while WPL-CF presents a different morphology with more irregular-shaped particles, probably due to its origin from wine seeds.
Figure 2 presents the TG (a) and the first derivative curves (b) for the two agro-wastes, GTF (black curve) and WPL-CF (purple curve). As is visible, the fillers show quite similar thermal behavior. The early weight loss was found at low temperature, 57 °C, and can be attributed to the desorption of moisture eventually absorbed on the biofillers' surfaces, which is more evident for GTF.
This can probably be explained by the fact that this filler is obtained by reusing corn wastes, which contain higher fractions of cellulose [[
WPL-CF powder starts to degrade at a lower temperature, 190 °C, and shows a first degradation peak at 272 °C and a second peak at 424 °C. However, the major difference in the thermal behavior of the two fillers is related to the residue content at 900 °C. GTF powder shows a residue of 6 wt.%, whereas for WPL-CF, a higher residue of 44 wt.% is found at the same temperature.
This can be attributed to the different origins of the two agro-waste fillers. GTF is derived from corn by-products, while WPL-CF is obtained from seed waste in wine production, which contains higher amounts of inorganic compounds.
AESO-based mixtures with biodegradable diluents, such as IBOMA and THFA, were first prepared by LCD 3D-printing technology. Then, the two different agro-wastes were added to the photocurable AESO-IBOMA and AESO-THFA mixtures at concentrations of 5 phr. All the tested AESO-based formulations are listed in Table 1. Before proceeding with the 3D-printing process of the AESO-based formulations, their viscosity was tested to evaluate the effect of the addition of reactive diluents to the resin flowability, which can significantly influence their final printability.
The results of viscosity tests of the AESO-based formulations containing IBOMA and THFA and of the composites obtained by adding 5 phr of the two agro-wastes are reported in Figure 3.
Figure 3a presents the rheograms of the unfilled and filled photocurable AESO-based formulations containing IBOMA. As expected, the zero-shear viscosity (
The values of viscosity obtained for samples containing IBOMA are considered useful for printable resin in the vat photopolymerization 3D-printing process. In fact, as reported in the literature, the optimal viscosities of a photocurable resin are usually set below 1000 cP [[
On the contrary, different behavior can be observed for samples obtained by dispersing the fillers within the AESO matrix in the presence of THFA as a diluent.
Figure 3b shows the values of zero-shear viscosity of the unfilled and filled AESO-THFA formulations, revealing that, for this kind of system, the viscosity values remain almost in the same range, being in any case acceptable for vat photopolymerization 3D printing.
The values of zero-shear viscosity increase from 355 cP to 400 cP for composites obtained by adding 5 phr of GTF. Indeed, a slight reduction in terms of viscosity can be observed for systems loaded with WPL-CF, from 355 to 290 cP, even if the photocurable formulations show a good dispersion and distribution of the fillers without any visible sedimentation. As is known from the literature, the viscosity range of photopolymers for LCD 3D printing typically falls in a medium-viscosity range (i.e., 100–500 cP). These viscosity values allow the resin to flow easily within the vat and spread over the platform or previous layers, requiring higher curing times, and reaching a balance between its flowability and printability. [[
Several preliminary printing tests were carried out to define the processing parameters and to assess the printability of the AESO-based resins with an LCD printer, guaranteeing the optimization of the photocuring process for the resins. The parameters optimized for the realization of the AESO-based formulations are summarized and listed in Table 2.
Furthermore, the presence of the biofillers led to an increase in the printing times and a decrease in the speed. This can be surely ascribed to the dye effect induced to the yellow (GTF) and purple (WPL-CF) powders introduced into the photocurable formulations [[
Having found the appropriate printing parameters for each formulation, different AESO-based polymer composite specimens were 3D printed, starting with simple geometry, like specimens rectangular in shape or dog bone shaped, up to more complex structures, like a gyroid cube reported in Figure 4 and a hexagon with singular internal pattern shown in Figure 5.
The sample shown in Figure 4 is rigid and shows a very good level of definition and a detail-rich shape, even on a very small scale. The specimen was successfully realized by the deposition of 300 layers of the AESO-IBOMA formulation. An example of a 3D-printed part obtained by adding THFA as diluent to the AESO matrix is shown in Figure 5, representing a complex hexagonal structure with a particular internal design where curvatures alternate full spaces. The hexagon is characterized by a very flexible structure, due to the intrinsic properties of THFA, and good, accurate print quality. It was obtained using LCD by depositing 80 layers of AESO-THFA.
Figure 6 and Figure 7 show pictures of specimens realized via LCD after the addition of the two different agro-wastes (GTF and WPL-CF) to the photocurable AESO-based formulations containing IBOMA and THFA, respectively. The pictures in Figure 6 represent typical hexagonal honeycomb-like cells made by the deposition of 4 and 80 layers of the AESO-based resin in the presence of IBOMA as a diluent (a) and of the relative composites filled with 5 phr of GTF (b) and WPL-CF (c). The samples reveal good dimensional and printing accuracy, also evidencing a significant change in color due to the presence of the fillers, which act as natural yellow (b) and purple (c)colorants, respectively.
Figure 7 shows examples of objects realized by LCD by adding the two agro-wastes at 5 phr within the AESO-based formulation containing THFA as the diluent. The specimens represent hexagons with intricate internal patterns with hollowed and thin interconnected walls, made by 4 and 80 layers of photocured resin (a). At the same time, Figure 7 illustrates hexagonal-shaped structures realized by photocuring AESO-based formulations containing THFA filled with the two kinds of agro-wastes, GTF (b) and WPL-CF (c). The 3D-printed objects realized even using an LCD 3D printer for the composites show high printing accuracy of small details and well-defined coloration induced to the presence of the biofillers, which can act as dye agents.
Photocured rectangular specimens showed high gel content after 24 h of extraction in chloroform at room temperature, with values of 99.5 and 99.9 wt.% for the AESO samples with IBOMA and THFA, respectively. The obtained results (Table 3) underline that the gel content values slightly decrease with the addition of biofiller particles. The results indicate that the amount of extractable monomers is very low, i.e., most of the reactive monomers are strongly linked to the photocured polymer network [[
The microstructure of the AESO-based composites realized by LCD was investigated by means of SEM (Figure 8). The analysis of the fracture surfaces of the AESO-based composites obtained by adding agro-wastes into the AESO resin revealed a better dispersion of the filler particles within the matrix in the case of the AESO-IBOMA system with respect to AESO-THFA.
In fact, the micrographs of Figure 8b,c show a uniform distribution and dispersion of the particles with the typical flake shape and good adhesion between the fillers and the matrix, as the fillers were still embedded in the crosslinked polymer matrix.
A certain number of agglomerates can be noticed, instead, for the composites obtained by dispersing the two biofillers into the AESO-THFA formulations. The presence of regions with micro-clusters of flakes is clear, particularly for composites loaded with WPL-CF, as reported in Figure 8e,f. This can be attributed to the higher time of exposure employed to print the series of composites containing THFA as diluent, due to its lower capacity to reduce the AESO viscosity (Table 1).
The thermal and viscoelastic properties of the AESO-based photocured samples and the relative composites were evaluated by means of TG and DMA analyses. Figure 9 presents the TG thermograms of the samples obtained by adding IBOMA (a) and THFA (b) as diluents and 5 phr of biofillers within the AESO matrix. The thermograms of the different systems present almost the same profile to underline that the presence of fillers did not impact the sample thermal stability, independently from the AESO/diluent mixture, as has already been reported [[
The TG curves of the photocured AESO-IBOMA resins showed two-stage degradation peaks, at around 320 and 380 °C, due to the scission of the ester bond of the iso-bornyl group [[
A significant difference between the two series of samples (AESO-IBOMA and AESO-THFA) can be found in the ash yield values, detected at 900 °C of the TG curves. If the addition of GTF led to a slight increase in the ash content percentage for both the systems, on the contrary, the dispersion of WPL-CF within the AESO-based resin induced a remarkable increase in the ash yield, as expected when evaluating the results obtained from the pure agro-waste (Figure 2).
In particular, the ash content percentage shifted from 1.5 to 3.6% for composites containing AESO+IBOMA and from 1.0 to 2.7% for those containing AESO+THFA (Table 3).
Furthermore, Figure 10 reports the comparison between the DMA curves of the crosslinked AESO-based samples containing IBOMA (a and b) and THFA (c and d) in the presence of the two biofillers. The unfilled samples presented completely different storage modulus values, 1633 MPa and 1040 MPa, respectively, for AESO-IBOMA and AESO-THFA, that once again underline the different effects induced to the reactive diluents to the AESO matrix. In fact, if IBOMA leads, at room temperature, to the formation of a rigid structure in the glassy state, THFA at room temperature gives rise to more flexible structures staying the rubbery region, as already seen for the 3D-printed samples reported in Figure 6 and Figure 7.
Meanwhile, the presence of the fillers within the AESO-IBOMA photocurable formulations allowed the elastic modulus to be enhanced in a significant way. In fact, the E' values, determined in the glassy state (0 °C), shifted from 1633 MPa to around 1850 MPa, probably due to the stiffening effect on the polymeric chains induced to the filler particles [[
DMA analysis also allowed us to achieve the exact monitoring of Tg values as maximum peaks of tan delta curves. A considerable increase in the Tg (about 30 °C; see Table 3) was achieved for AESO-IBOMA composites due to the reinforcement effect induced by the presence of the biofillers, which led to restrictions of the polymeric chain motions. Moreover, the increase in the glass transition towards higher temperatures underlined the formation of a more rigid structure. On the contrary, a decrease in Tg values (Table 3) was observed for the composites obtained starting from AESO-THFA photocurable samples, as already seen for the storage modulus values.
This can be explained by considering the flexibility effect due to the biofiller particles on the polymer matrix mixed with THFA. Furthermore, it is possible to see that the tan delta curves exhibited a broader profile indicative of poor adhesion between the layers occurring during the printing process [[
Finally, the tensile properties at room temperature of the photocured AESO-based specimens were investigated by tensile tests. Elastic modulus, tensile strength, and elongation at break values, in percentages, were determined from their stress–strain curves and are summarized in Table 4. The results of the tests indicate, as expected, that the tensile properties of the AESO-IBOMA and AESO-THFA samples at room temperature were totally different. The values of elastic modulus, tensile strength, and elongation at break of AESO-IBOMA were more than one order of magnitude higher than that of the AESO-THFA, and this was strictly dependent on the reactive diluent characteristics.
However, analyzing the values of the tensile properties of the AESO-based composites filled with the agro-wastes, it was possible to see that a significant increase in the Young's modulus and tensile strength occurred for samples realized by the LCD 3D printer by adding the two agro-wastes fillers into the formulations prepared by mixing AESO with IBOMA as a reactive diluent. This could certainly have been due to the rigid iso-bornyl group which led the photo-crosslinked polymers to be stiffer and inflexible, also suggesting good adhesion among the printed layers [[
A completely different situation can be seen for the AESO-THFA specimens. In this case, the AESO-THFA resins showed lower mechanical properties, giving rise to the formation of soft and flexible specimens. Furthermore, the addition of the biofillers did not affect the final mechanical properties in a positive way, which remained almost the same. This could most likely have been due to the presence of agglomerates of filler particles within the polymeric matrix, as already seen from SEM micrographs, leading to a decrease in the elasticity and tensile strength, increasing the polymer chain flexibility [[
Considering the results obtained, it can be concluded that AESO-based polymers demonstrate tunable properties, varying from rigid to flexible, in the presence of different diluents (IBOMA and THFA) and biofillers (GTF and WPL-CF). The comparison of the tensile properties between the two series of specimens clearly evidenced that the AESO-IBOMA system gave rise to the best mechanical properties, suggesting that it was characterized by a very highly crosslinked structure and can be used with success for the realization of structural 3D-printed parts by LCD.
Figure 11 reports two examples of components printed starting from the AESO-IBOMA system that can be used for biomedical applications.
The pictures in Figure 11a,b show two different views of a prosthesis for a human anatomy-based metacarpal hand designed to help people with missing fingers. The sample referred to the AESO-IBOMA+5GTF formulation. Figure 11c,d present a typical prosthesis for a pug dog that had completely lost a left front limb, realized by LCD with reference to the AESO-IBOMA+5WPL-CF formulation. The components show a very good level of definition and high dimensional stability.
The present work focused on the preparation of bio-based polymer composites by LCD as a 3D-printing process by means of the addition of two different agro-waste fillers, GTF and WPL-CF, obtained by corn and wine production wastes, within renewable soybean oil-based photocurable formulations, in the presence of two reactive diluents, IBOMA and THFA.
The comparison between the two kinds of resin systems, AESO-IBOMA and AESO-THFA, revealed significant differences. First, the zero-shear viscosity of the AESO-based photocurable formulations increased in the presence of agro-wastes for mixtures with IBOMA, reaching ideal values for printable resin in the vat polymerization 3D-printing process. Once the viscosity was evaluated and the optimal printing parameters were set, several 3D-printed components with different geometries and complexities were realized by LCD with and without fillers, such as gyroid cube, hexagon with intricate internal design, or hexagonal honeycomb-like cell structures made by the deposition of a high number of layers during the VP process. The composites prepared by adding the two different fillers at 5 phr within the polymeric matrix were fully characterized from the morphological, thermal, and mechanical points of view.
The results obtained revealed that agro-wastes' addition into the AESO-based matrix induced a significant increase in the elastic modulus, tensile strength, and glass transition temperature values, especially for the mixtures containing IBOMA as the reactive diluent. This can be attributed to a stiffening effect induced to the presence of the filler particles which acted as reinforcing agents. The biofillers also gave rise to characteristic yellow and purple pigmentation in the specimens due to their dye action within the photocured resin. In contrast, the addition of the two fillers did not have an effect on the thermal stability of the composites, which showed almost the same thermal behavior. This finding allowed us to conclude that strong crosslinked structures can be obtained by LCD, giving rise to structural 3D-printed parts with very highly detailed architectures useful for applications in the biomedical field. A prosthesis for a human metacarpal hand, obtained by dispersing 5 phr of GTF within the AESO-IBOMA resin, and a pug dog prosthesis filled with 5 phr of WPL-CF powder were also successfully realized.
This study undoubtedly deserves further investigations to evaluate the biodegradability, cytotoxicity, and cell proliferation of the obtained photocured samples, as well as to optimize the 3D-printing process to develop even more complex 3D structures.
This research can significantly enhance the use of bio-based and renewable materials for the 3D printing of parts for biomedical applications using LCD as the vat polymerization technique. In addition, the use of biofillers can valorize agricultural wastes, reducing costs and promoting the development of a new generation of 3D-printed biodegradable composite materials with additional environmentally friendly impacts for the future.
Graph: Figure 1 SEM micrographs at different magnifications of GTF (a) and WPL-CF (b).
Graph: Figure 2 TG (a) and DTG (b) curves of GTF and WPL-CF powders, performed in air.
Graph: Figure 3 Rheograms (viscosity vs. shear rate) of AESO-based liquid formulations based on IBOMA (a) and THFA (b).
Graph: Figure 4 Gyroid cube-shaped 3D-printed sample based on AESO-IBOMA.
Graph: Figure 5 Hexagonal-shaped, 3D-printed sample based on AESO-THFA.
Graph: Figure 6 Three-dimensionally printed AESO-based samples with different dimensions: (a) AESO-IBOMA, (b) AESO-IBOMA+5GTF, and (c) AESO-IBOMA+5WPL-CF.
Graph: Figure 7 Three-dimensionally printed AESO-based samples with different dimensions: (a) AESO-THFA, (b) AESO-THFA+5GTF, and (c) AESO-THFA+5WPL-CF.
Graph: Figure 8 Three-dimensionally printed AESO-based specimens' micrographs: (a) AESO-IBOMA, (b) AESO-IBOMA+5GTF, (c) AESO-IBOMA+5WPL-CF, (d) AESO-THFA, (e) AESO-THFA+5GTF, and (f) AESO-THFA+5WPL-CF.
Graph: Figure 9 TG and DTG curves of 3D-printed samples containing IBOMA (a,b) and THFA (c,d) unfilled and filled with agro-wastes.
Graph: Figure 10 DMA curves of 3D-printed samples containing IBOMA (a,b) and THFA (c,d) with and without biofillers.
Graph: Figure 11 Three-dimensionally printed AESO-based components prepared with IBOMA for biomedical application, representing a human metacarpal hand prosthesis with GTF (a,b) and a pug dog prosthesis with WPL-CF (c,d).
Table 1 Composition of photocurable AESO-based liquid formulations.
Sample Code AESO (wt.%) Diluent (wt.%) Biofiller (phr) AESO-IBOMA 60 40 0 AESO-IBOMA+5GTF 60 40 5 AESO-IBOMA+5WPL-CF 60 40 5 AESO-THFA 60 40 0 AESO-THFA+5GTF 60 40 5 AESO-THFA+5WPL-CF 60 40 5
Table 2 Printing parameters for AESO-based resins printed by LCD 3D printer.
Parameter AESO-IBOMA AESO-IBOMA +5GTF AESO-IBOMA AESO-THFA AESO-THFA +5GTF AESO-THFA 0.1 0.1 0.1 0.1 0.1 0.1 12 18 18 18 25 25 30 40 40 40 45 45 0 3 3 0 5 5 4 8 8 5 8 8 3 6 6 3 6 6 7 8 8 6 8 8 6 8 8 6 8 8 7 8 8 6 8 8 6 8 8 6 8 6 60 50 50 90 70 70 60 50 50 90 70 70 150 130 130 170 150 150 150 130 130 170 150 150
Table 3 Gel %, thermal, and viscoelastic properties of AESO-based samples.
Sample Gel Tonset Tmax deg Ash E′@ 0 °C Tan Delta AESO-IBOMA 99.5 297 320–380 1.5 1633 51 AESO-IBOMA 99.5 292 320–380 1.8 1855 80 AESO-IBOMA 98.5 285 320–380 3.6 1846 76 AESO-THFA 99.9 304 393 1.0 1040 22 AESO-THFA 99.1 308 384 1.2 308 15 AESO-THFA 99.6 296 378 2.7 309 12
Table 4 Tensile properties of AESO-based samples.
Sample Young's Modulus (MPa) Tensile Strength (MPa) Elongation at Break (%) AESO-IBOMA 443 ± 25 16 ± 0.5 12 ± 3.0 AESO-IBOMA 987 ± 42 30 ± 0.1 6 ± 0.7 AESO-IBOMA 933 ± 34 27 ± 1.6 5 ± 0.7 AESO-THFA 15 ± 1.0 3 ± 1.2 22 ± 9.0 AESO-THFA 15 ± 0.4 2 ± 0.3 13 ± 2.0 AESO-THFA 15 ± 0.6 2 ± 0.3 15 ± 2.0
Conceptualization, G.C. and M.M.; methodology, G.C.; validation, G.C., formal analysis, G.C. and F.S.; investigation, G.C. and F.S.; resources, F.B. and M.M.; data curation, G.C. and F.S.; writing—original draft preparation, G.C.; writing—review and editing, G.C., F.S., M.M. and F.B.; visualization, G.C. and M.M.; supervision, F.B. and M.M.; project administration, F.B.; funding acquisition, F.B. and M.M. All authors have read and agreed to the published version of the manuscript.
Not applicable.
Data are contained within the article.
The authors declare no known conflicts of interest or personal relationships that could have influenced the work reported in this paper.
The author would like to thank Sebastiano Fattoruso for his kind support.
By Giovanna Colucci; Francesca Sacchi; Federica Bondioli and Massimo Messori
Reported by Author; Author; Author; Author