Evaluating the Effects of Sandblasting on Micro-Shear Bond Strength and Flexural Strength of Zirconia
In: Majallah-i Dānishgāh-i ̒Ulūm-i Pizishkī-i Bābul, Jg. 24 (2022), Heft 1, S. 435-443
Online
academicJournal
Zugriff:
Background and Objective: Various techniques have been introduced to improve bond strength of zirconia which may negatively affect flexural strength. This study aims to evaluate the effects of different sandblasting parameters on micro-shear bond strength (MSBS, Mpa) and biaxial flexural strength (BFS, Mpa) of Zirconia. Methods: In this in vitro study, zirconia blocks were cut into 180 discs for MSBS and BFS tests (90 specimens in each group). For each test, they were divided into one control group and 8 experimental groups according to the type of sandblasting regimen (pressures of 4 or 6 bar, duration of 14 or 21 seconds, and alumina powder sizes of 50 or 110 μm, n=10). A universal testing machine was used to determine MSBS and BFS. X-ray diffraction (XRD) analysis was then performed. Findings: According to the results, groups with 110 μm particles (4 bar- 14 s, 6 bar- 14 s, 4 bar- 21 s and 6 bar- 21 s with MSBS values of 34.43±5.99, 35.21±6.39, 27.17±3.95 and 28.66±3.92 Mpa, respectively) had significantly higher MSBS values compared to the control group (p
Titel: |
Evaluating the Effects of Sandblasting on Micro-Shear Bond Strength and Flexural Strength of Zirconia
|
---|---|
Autor/in / Beteiligte Person: | Majidinia, S ; Bagheri, H ; M Maghsoudlou Nejad ; Shekofteh, K ; Parhizkar, T |
Link: | |
Zeitschrift: | Majallah-i Dānishgāh-i ̒Ulūm-i Pizishkī-i Bābul, Jg. 24 (2022), Heft 1, S. 435-443 |